Product Description Sheet

LOCTITE® EA 0151

Known as

Hysol Product 0151®

August 2015

Description Shear Strength, psi, ASTM D 1002 Etched Aluminum

® o

LOCTITE EA 0151 is a clear two-component epoxy having Cure Schedule Test Temp F Typical Value

® o

optical clarity when used in small quantities LOCTITE EA 0151 3 Days @ 77F -67 1600is easy to mix and has a long pot life. 77 1850

180 400

2 Hours @ 140 F o -67 2700Recommended Substrates: Glass, Metals, Circuit Boards, 77 3000Fiber Optics and many Plastics. 180 600

1 Hour @ 180 F o -67 2700Features 77 3000Clear Color 180 500RT or Heat Cure

Bonds Many Materials Outgassing Performance NASA 1124Easy to Mix Total Mass Loss, % 1.51100% Solids Collected Volatile Condensable Material, % 0.01Thixotropic Paste

Handling

Mixing: This product requires mixing two components togetherTypical Uncured Part A Part B Mixed just prior to application. Complete mixing is necessary. TheProperties temperature of the separate components prior to mixing is notPot Life @ 77°F, 100 -- -- 60 critical, but they should be close to room temperature.grams mins

Color Milky White Amber Clear Application

Viscosity, cP 40,000 to 20,000 to -- Mixing - Bulk: Combine Part A (resin) and Part B (hardener) in

100,000 100,000 the correct ratio and mix thoroughly until the color andSpecific Gravity 1.13 0.98 -- consistency are uniform. EPOXI-PATCH® Tube Kits have beenMix Ratio designed so that squeezing EQUAL LENGTH BEADS of Part A

By weight 100 33 & Part B will give proper ratio. Ratios given above can be used

By volume 2.7 1 for measuring larger amounts. Mixing the adhesive just prior to

use is recommended. Heat buildup during or after mixing is

normal. Do not mix quantities greater than two pounds as

dangerous heat buildup can occur causing uncontrolledTypical Properties Typical Value decomposition of the mixed adhesive. Mixing smaller quantitiesTensile Strength, psi, ASTM D 638 -- will minimize the heat buildup.

Elongation, %, ASTM D 638 2.4 Mixing - Cartridges: Place cartridge in proper dispenser. ToTg, °F 136 begin using a new cartridge, remove cartridge cap and dispenseCTE, ASTM D 696, in/in/ °C 47 x 10-6

2 -4 a small amount of adhesive, making sure both Parts A & B areThermal Conductivity, cal x cm/cm x 5.6 x 10 extruding. Attach nozzle and dispense approximately 1-2"secs x °C before applying onto the part to be bonded. Partially usedShrinkage, % <0.3 cartridges can be stored with the mixing nozzle attached. ToHardness, Shore D 85 reuse, remove and discard the old nozzle, attach the new nozzle,

and begin dispensing.

**Note** Mix cartridge dispenses adhesive in a 2:1 ratio.

Tests show no significant effect on bondElectrical Properties Typical Value performance compared to 2.7:1 ratio.

Dielectric Strength, ASTM D149, V/mil 1080 Application: Bonding surfaces should be clean and dry. OnceDielectric Constant, MIL 1-16923. K 1kHz 3.88 the adhesive is applied, the bonded parts should be held inDissipation Factor, ASTM D 150 1kHz 5.3 x 10-4 contact until the part has developed handling strength. It is not

+15 necessary to clamp the parts unless movement during cure isVolume Resistivity, ASTM D 257 ohm/cm 1.26 x 10

Surface Resistivity, ASTM D 257 -- likely.

Product Description Sheet

LOCTITE® EA 0151

Known as

Hysol Product 0151®

August 2015

Cure: Complete cure is obtained after three days at room merchantability or fitness for a particular purpose, arising from saletemperature. After 24 hours, approximately 90% of full cure or use of Henkel Corporation’s products. Henkel Corporationproperties are attained. Hysol 0151 will achieve handling specifically disclaims any liability for consequential or incidentalstrength in 6-8 hours at 77°F (note: this can vary with different damages of any kind, including lost profits. The discussion herein ofbond configurations). Hysol 0151 can also be completely cured various processes or compositions is not to be interpreted aswith heat such as: 2 hours at 140°F; 1 hour at 180°F; or 30 representation that they are free from domination of patents owned byminutes at 250°F. Heat cures can be modified to achieve a others or as a license under any Henkel Corporation patents that maydesired degree of cure from handling strength to full cure. corovser stuich upsreorc teessst ehsi opr ocosmepdo sitipolincs. ioWn e rfeocro mrempeetnitdi that each

use, using this data as a guide. This product may be covered by one orClean Up: It is important to remove excess adhesive from the more United States or foreign patents or patent applications.work area and application equipment before it hardens. Many In case products are delivered by Henkel Belgium NV, Henkelcommon solvents and citrus cleaners are suitable for removing Electronic Materials NV, Henkel Nederland BV, Henkel Technologiesuncured adhesive. Consult with your supplier's information France SAS and Henkel France SA please additionally note thepertaining to the safe and proper use of solvents. following:

In case Henkel would be nevertheless held liable, on whatever legalStorage ground, Henkel’s liability will in no event exceed the amount of the

concerned delivery.

Store product in unopened container in a cool dry location. Ideal In case products are delivered by Henkel Colombiana, S.A.S. theconditions are within the range 8 to 21 degrees C (46 to 70 following disclaimer is applicable:

degrees F) and are recommended for long term storage. The information provided in this Technical Data Sheet (TDS) includingExposure to higher temperatures (greater than 28 degrees C) for the recommendations for use and application of the product are basedprolonged periods should be avoided as extended exposure to on our knowledge and experience of the product as at the date of thiswarm conditions can adversely affect product properties. For TDS. Henkel is not liable for the suitability of our product for thefurther specific shelf life information, contact your local Technical production processes and conditions in respect of which you use them,Service Center. as well as the intended applications and results. We strongly recommend

that you carry out your own prior trials to confirm such suitability of our

product.

Note Any liability in respect of the information in the Technical Data Sheet orThe information provided in this Technical Data Sheet (TDS) including any other written or oral recommendation(s) regarding the concernedthe recommendations for use and application of the product are based product is excluded, except if otherwise explicitly agreed and except inon our knowledge and experience of the product as at the date of this relation to death or personal injury caused by our negligence and anyTDS. The product can have a variety of different applications as well as liability under any applicable mandatory product liability law.differing application and working conditions in your environment that are

beyond our control. Henkel is, therefore, not liable for the suitability of our Trademark usage

product for the production processes and conditions in respect of which Except as otherwise noted, all trademarks in this document areyou use them, as well as the intended applications and results. We trademarks of Henkel Corporation in the U.S. and elsewhere. ® denotesstrongly recommend that you carry out your own prior trials to confirm a trademark registered in the U.S. Patent and Trademark Office.such suitability of our product.

Any liability in respect of the information in the Technical Data Sheet or

any other written or oral recommendation(s) regarding the concerned

product is excluded, except if otherwise explicitly agreed and except in

relation to death or personal injury caused by our negligence and any

liability under any applicable mandatory product liability law.

In case products are delivered by Henkel Corporation, Resin

Technology Group, Inc., or Henkel Canada, Inc.the following disclaimer

is applicable:

The data contained herein are furnished for information only and are

believed to be reliable. We cannot assume responsibility for the results

obtained by others over whose methods we have no control. It is the

user's responsibility to determine suitability for the user's purpose of any