 TechnicalDataSheet

    LOCTITE® SI 5031™

    KnownasLOCTITE®5031™

    January-2015PRODUCTDESCRIPTION    DepthofCure

    ®    Depthofcure,mm:

LOCTITE   SI  5031™  provides  the  following  product

    90 seconds@70 mW/cm²,measured@365≥20LMS

characteristics:    nm

Technology    Silicone

ChemicalType    Acetoxydualcuresilicone    DepthofCure(light)

Appearance(uncured)  Light yellow,translucent liquidLMS    RapiddepthofcurecanbeattainedwithfocusedUVand/or

    LMS    visiblelight.ThefollowinggraphshowsthecureresponseofFluorescence    Positive underUVlight    sometypicallightsourcesasafunctionofirradianceafter60Components    One component -    seconds.Thefollowingdatatableshowsthedepthofcure

    requiresnomixing    obtained upon exposure to different light sources andCure    Ultraviolet(UV)/visiblelight    intensitiesovertime.

SecondaryCure    Moistureforshadowedareas

Application    Potting,Coating orSealing    45

Self-leveling    Uniformcavityfill    lb

    Bu

    40    V

    ®

LOCTITE  SI5031™isaflowablesealantwiththebenefitof    m

    m35    15

    72

deeplightcurecapability,ultravioletandvisible,combinedwith    ,  30

    e

asecondary moisture cure mechanism for shadow curing.    r

    u 25

Upon exposure to sufficient UV light, visible light  or    C

    D

    f    B

    20    ulatmosphericmoisture,thisproduct formsamediumstrength,    o    b

    20    H

    74    B

    h    u

    t  15    lb

flexiblerubbersealant.

    p

    e 10

TYPICALPROPERTIESOFUNCUREDMATERIAL    D

 SpecificGravity@ 25°C    1.0    5

 Solids/Non-VolatileContent,%    96.9    0

 AspectRatio@60 seconds,Height/Width    0.1    0    40    70    130    180

    Irradiance, mW/cm²

 FlashPoint-SeeSDS

 Viscosity,Brookfield -RVT, 25°C,mPa·s(cP):

  Spindle3,speed10rpm,    4,000 to7,500LMS

    Irradiance       DepthofCure,mm

    LightSource                UV/VIS       30sec.   60sec.  90sec.TYPICALCURINGPERFORMANCE

Normalprocessingconditionswillincludeexposuretosufficient    7411UV(metalhalide)    179/58             7.4        23.2      31.1UV lightirradiancetoeffectivelycurethematerial. Surface    7411V(visible    40/98              8.2        20.2      23.4and/oratmosphericmoisturewillpromotethecureofmaterial    enhancedmetalhalide)

in  shadowed  regions.  Although  functional  strength  is    7r2e1s5s(3re00-wgaatrtcm)edium   75/95             23.3        33.2      40.7developedalmostinstantlyduetotheUV curing natureof    ElectrodelessVbulb    71/124           16.8        27.9      39.2

    ®    Electrodeless Dbulb    76/50             10.1        22.2      33.4LOCTITE SI5031™,increasedcurepropertiesaredeveloped    Electrodeless Hbulb    71/68              4.6        15.8      23.9during72hoursatambientconditions.    Electrodeless H+bulb    74/64              8.5        20.9      28.0SurfaceCure    7735(50-watt high    890/410            ---        13.3      17.2SkinOverTime    pressureHgarc)

Skinovertimeisthetimethesurfaceoftheadhesiveformsa    7r7e4s0s(1re00-wgaatrt h)igh    797/414           2.5        14.3      17.2skinuponexposuretoatmosphericmoistureat25±2°C,50±    7760(200-watt high    1,146/459          ---          9.2      12.85%RH.    pressureHgarc)

 SkinOverTime, minutes:    7700(LED)    12/31                ---          8.0      13.4

    LMS    7420 (visiblearclamp)    20/40              8.0          ---       26.7Cured@23°C    ≤20

TackFreeTime    7500 (fluorescentlamp)   40/0                 ---          2.1       4.2TackFreeTimeisthetimerequired toachieve atackfreesurface    Note:Irradiancemeasuredwith7011-A(UV)&7011-V(VIS)TackFreeTime, ASTMC679, seconds:    dosimeters

   70 mW/cm²,measured@365nm    ≤20

    TDSLOCTITE®SI5031™,   January-2015DepthofCure(moistureonly)    AcomparisonofthecompressionsetversusmoisturecureMoisture cure of shadowed areas rely on surface and/or    conditionisshowninthegraphbelow.

atmosphericmoisturetoeffectcure.Thetypicaldepthofcure    Cured @ 70 mW/cm², measured @ 365 nm, for 60 secondsfrom moistureonly versus time(days) at25 °C and 50%    Compressionsetmeasuredafterbeingaged@22°Cfor70hoursrelativehumidityisshowninthegraphbelow.

    18    25

    16    ,%20

  m14    t

    e

  m

    S

  ,  12

  e

    n 15

  r

    o

  u 10    i

    s

  C

    s

  f

    8    e 10

  o    r

    p

  th  6

    m

  p

  e    o  5

    4

    C

  D  2

    0    0

    0  2  4  6  8 10 12 14 16 18 20 22 24 26 28    0  1  2  3  4  5  6  7  8  9 10 11 12 13 14

    Cure Time, days    Secondary Moisture Cure Time, daysTYPICALPROPERTIESOFCUREDMATERIAL    TYPICALPERFORMANCEOFCUREDMATERIALCured@70mW/cm², measured @365nm,for60 seconds perside    AdhesiveProperties

 , followedby72 hours@23°C/50%RH

  PhysicalProperties:    Cured @ 70 mW/cm², measured @ 365 nm, for 60 seconds

   CoefficientofThermalExpansion,    354×10-6     followedby72 hours@23°C/50%RH,(Isopropylalcoholwiped

   ISO11359-2,K-1    substrates)

   WaterVaporTrans.Rate,ASTME96,g/(h·m²)    3.03    LapShearStrength,ISO4587:

   WaterAbsorption,ISO62,%:    Aluminum(Alclad)  toGlass    N/mm²   2.0

    24 hoursinwater @23°C    0.15    (psi)       (295)

   VolumeShrinkage,ASTMD792,%    0.32    Steel  toGlass    N/mm²   1.3

   LinearShrinkage,ASTMD792,%    0.11    (psi)       (180)

    LMS    Glass  toGlass    N/mm²   2.1

   ShoreHardness, ISO868,DurometerA    28 to40    (psi)       (305)

   Elongation,atbreak,ISO37,%    ≥60LMS

    LMS    Polycarbonate toPolycarbonate    N/mm²   0.1

   TensileStrength,ISO37    N/mm²   ≥0.55    (psi)       (10)

    (psi)       (≥79)    Polycarbonate toGlass    N/mm²   0.5

   TearStrength, ISO34-1 ,DieC    N/mm     1.7    (psi)       (65)

    (lb./in.)   (9.7)    Polycarbonate  toAluminum    N/mm²   0.2

   GasPermeability,ASTMD1434,cm²/sec/atm:    (psi)       (25)

    -6    Polycarbonate  toSteel    N/mm²   0.5

    Oxygen    6.37×10    (psi)       (70)

    Hydrogen    6.76×10-6

    -5    PVC  toGlass    N/mm²   0.8

    CarbonDioxide    3.45×10    (psi)       (120)Electrical Properties:    PVC  toPolycarbonate    N/mm²   0.4

    14    (psi)       (55)

   VolumeResistivity,IEC60093,Ω·cm    2.5×10    Polybutylene    N/mm²   0.8

   DielectricBreakdownStrength,    20.3    Terephthalate(PBT)  toGlass    (psi)       (115)

   IEC60243-1,kV/mm    Polybutylene    N/mm²   0.2

   DielectricConstant/DissipationFactor,IEC60250:    Terephthalate(PBT)  toPolycarbonate       (psi)       (30)

    1-kHz    2.85/0.008    ABS  toGlass    N/mm²   0.4

    1-MHz    2.85/0.005    (psi)       (55)

    ABS  toPolycarbonate    (Np/smi)m    ²    04.3)Cured@70mW/cm², measured @365nm,for 60 seconds per    Nylon  toGlass    N/mm²   0.5side, followedby14 days@23°C/50%RH    (psi)       (75)PhysicalProperties:    Nylon  toPolycarbonate    N/mm²   0.1

   CompressionSet,ASTMD395,MethodB,%:    (psi)       (15)

    Aged@22°Cfor70 hours    4.7

    Aged@70°Cfor22 hours    9.0

    Aged@121°Cfor22 hours    29.1

    Aged@150°Cfor22 hours    45.4

Henkel Americas    Henkel Europe    Henkel AsiaPacific+860.571.5100    +49.89.320800.1800    +86.20.3623.0506

    Forthemostdirectaccesstolocalsalesandtechnicalsupportvisit:loctite.net    TDSLOCTITE®SI5031™,   January-2015ShearStrength vs.GapThickness    ASTMIRM901oil:

 Cured @ 70 mW/cm², measured @ 365 nm, for 60 seconds    ChangeinDurometer,Points(Initial=36)    -21followedby7 days@23°C/50%RH    ChangeinTensileStrength,%    30.6

    ChangeinElongation,%    325

    2.5    VolumeSwell,%    5.9²    ASTMIRM902oil:

  m    A

    lum

  m2.0    ChangeinDurometer,Points(Initial=36)    -13

    in

  /    u

    m

  N    (

    Alc    ChangeinTensileStrength,%    -16.1-    l

    G    a

    l    d

    1.5   a    )    ChangeinElongation,%    23.4h    ss

  t    VolumeSwell,%    8.3

    St

    e

  n    e

    l    Polypropylene

  re    ®

    1.0

  t    ATF(Dexron III):

  S    ChangeinDurometer,Points(Initial=36)    -31r

  a 0.5    ChangeinTensileStrength,%    -61.0e

  h    ChangeinElongation,%    93.9S    VolumeSwell,%    23.2

    00    0.25    0.50    0.75    1.0

    Gap, mm

    GENERALINFORMATION

TYPICALENVIRONMENTAL RESISTANCE    ThisproductisnotrecommendedforuseinpureoxygenCured@70mW/cm², measured @365nm,for60 seconds perside    and/oroxygenrichsystemsandshouldnotbeselectedas, followedby7 days@23°C/50%RH    asealantforchlorineorotherstrongoxidizing materials.HeatAging    Forsafehandlinginformationonthisproduct,consulttheAgedattemperatureindicatedandtested@22°C    SafetyDataSheet(SDS).

 Aged@177°Cfor168 hours:

  ChangeinDurometer,Points(Initial=36)    -8    Directionsforuse:

  ChangeinTensileStrength,%    -6.3    1. Thisproductislight sensitive; exposuretodaylight,UVChangeinElongation,%    17.9    lightandartificiallightingshouldbekepttoaminimumWeightLoss,%    -3.4    duringstorageandhandling.

 Aged@233°Cfor168 hours:    2. TheproductshouldbedispensedfromapplicatorswithChangeinDurometer,Points(Initial=36)    24    blackfeedlines.

  ChangeinTensileStrength,%    60.9    3. ForbestperformancebondsurfacesshouldbecleanandChangeinElongation,%    -66.2    freefromgrease.

  WeightLoss,%    -3.3    4. Theproductisdesignedtobeinitiallycured byUV/visible

    light at a minimum irradiance of 30 mW/cm2 forTypicalFluidImmersionProperties    approximately 20 seconds, increasedexposuremaybeAged@100°Cfor168 hours:    requiredforcuringdeepersections.

  Ethyleneglycol/water,50:50:    5. Functionalstrengthisachievedalmostinstantly.

   ChangeinDurometer,Points(Initial=36)    -14    6. Fullperformancepropertieswilldevelopover72hours.

   ChangeinTensileStrength,%    -42.6    7. Moisturecuringbeginsimmediatelyafter theproductis

   ChangeinElongation,%    25.1    exposed to the atmosphere, therefore parts to be

   VolumeSwell,%    -1.5    assembledshouldbematedwithinafewminutesafterthe

    productisdispensed.

  Propylene glycol/water(Dex-Cool®),50:50:

   ChangeinDurometer,Points(Initial=36)    -16    8. sExlcveesnstsm.aterialcanbeeasilywipedawaywithnon-polar

   ChangeinTensileStrength,%    -28.8

   ChangeinElongation,%    42.3    LoctiteMaterialSpecificationLMS

   VolumeSwell,%    -1.9    LMSdated May-17,2005. TestreportsforeachbatchareAged@150°Cfor70 hours:    availablefortheindicatedproperties. LMStestreportsincludeASTMIRM903oil:    selected QC test parameters considered appropriate to

   ChangeinDurometer,Points(Initial=36)    -20    specificationsforcustomeruse. Additionally,comprehensive

   ChangeinTensileStrength,%    -26.0    controls  are in place to assure product quality and

   ChangeinElongation,%    13.8    consistency. Specialcustomerspecificationrequirementsmay

   VolumeSwell,%    47.4    becoordinatedthroughHenkel Quality.

 Aged@150°Cfor168 hours:

  5W30oil:

   ChangeinDurometer,Points(Initial=36)    -31

   ChangeinTensileStrength,%    -55.3

   ChangeinElongation,%    20.3

   VolumeSwell,%    24.9

Henkel Americas    Henkel Europe    Henkel AsiaPacific+860.571.5100    +49.89.320800.1800    +86.20.3623.0506

    Forthemostdirectaccesstolocalsalesandtechnicalsupportvisit:loctite.net    TDSLOCTITE®SI5031™,   January-2015Storage    disclaims allwarrantiesexpressedorimplied, includingwarrantiesofStoreproductintheunopenedcontainer inadry location.    merchantabilityorfitnessforaparticularpurpose,arisingfromsaleoruseStorageinformationmaybeindicatedontheproductcontainer    of Henkel Corporation’s products. Henkel Corporation specifically

    idnislcladiimnsalnoystliabilitiytf.orchoenseiqsuceunstiialnorhienrceiidentfalvdaarmioagesprofcanyeksindr,labeling.    compositionsisnottobeinterpretedasrepresentationthattheyarefreefromOptimalStorage: 8°Cto21°C. Storagebelow 8°Cor    dominationofpatentsownedbyothersorasalicenseunderanyHenkelgreaterthan28°Ccanadverselyaffectproductproperties.    Corporation patents that maycoversuch processesor compositions. WeMaterialremovedfromcontainersmaybecontaminatedduring    recommendthateachprospectiveusertesthisproposedapplicationbeforeuse. Donotreturnproducttotheoriginalcontainer.  Henkel    repetitiveuse,usingthisdataasaguide.ThisproductmaybecoveredbyoneorCorporationcannotassumeresponsibilityfor product which    moreUnitedStatesorforeignpatentsorpatentapplications.

hasbeencontaminatedorstoredunderconditionsotherthan    Trademarkusage

thosepreviouslyindicated.Ifadditionalinformationisrequired,    Exceptasotherwisenoted,alltrademarksinthisdocumentare trademarksofplease contact your local Technical Service Center  or    HenkelCorporation in theU.S. andelsewhere.   ® denotesa trademarkCustomerServiceRepresentative.    registeredintheU.S.PatentandTrademarkOffice.

Conversions

(°Cx1.8)+32=°F    Reference1.2

kV/mmx25.4=V/mil

mm/25.4=inches

µm/25.4=mil

N/x0.2x25.=lb=lb/in

N/mm²x145=psi

MPax145=psi

N·m x 8.851= lb·in

N·mx0.738=lb·ft

N·mm x0.142=oz·in

mPa·s=cP

Note:

Theinformation provided inthisTechnicalData Sheet(TDS)includingthe

recommendationsforuseandapplicationoftheproductarebased onour

knowledgeandexperienceoftheproductasatthedateofthisTDS.Theproduct

caonrkihnavecoanviatirientyiofydiffrereenntiraopnplicanttiotnstaasrewellyaosnddifferincgonatrpopllicHationelanisd,

therefore,notliableforthesuitabilityofourproductfortheproductionprocesses

andconditionsinrespectofwhichyouusethem,aswellastheintended

applicationsandresults.Westronglyrecommendthatyoucarryoutyourown

prioyrltriaillsittoincorenfiremctsuocfhthseuitafbilityatoifouirptroduct.hnicalDataSheetoranyother

writtenororalrecommendation(s)regardingtheconcernedproductisexcluded,

exceptifotherwiseexplicitlyagreedandexceptinrelationtodeathorpersonal

injurycausedbyournegligenceandanyliabilityunderanyapplicablemandatory

productliabilitylaw.

InatcearsielsproVd,uctsnarleNdeelievrelreddbByV,HenkellBTelgiunmoloNgVi,sHernakeleElectroannic

HenkelFranceSApleaseadditionallynotethefollowing:

IncaseHenkelwouldbeneverthelessheldliable,onwhateverlegalground,

Henkel’sliabilitywillinnoeventexceedtheamountoftheconcerneddelivery.

IncaseproductsaredeliveredbyHenkelColombiana,S.A.S.thefollowing

diseclaiifmoreristioanpplicoavible: inthisTechnicalData Sheet(TDS)includingthe

recommendationsforuseandapplicationoftheproductarebased onour

knowledgeandexperienceoftheproductasatthedateofthisTDS.Henkelis,

therefore,notliableforthesuitabilityofourproductfortheproductionprocesses

andliccaotnioditionsdinrereusltpse.cteofstwrohicghlyyroeucouseethdemt,atasowuellrrasthteyinternoded

priortrialstoconfirmsuchsuitabilityofourproduct.

AnyliabilityinrespectoftheinformationintheTechnicalDataSheetoranyother

writtenororalrecommendation(s)regardingtheconcernedproductisexcluded,

ienxjcreyptifuosthderbwyisoeurexeplilciitlynacgraeedaannydlieaxbcileitpytindreelatioyntopldiecathleorapnersaotnral

productliabilitylaw.

IncaseproductsaredeliveredbyHenkelCorporation,ResinTechnology

Group,Inc.,orHenkelCanadaCorporation,thefollowingdisclaimeris

applicable:

Teheredliaatbalc.ontaeinceadnhoetreinsaurefurrenisphoendsifboilritinfforrmtatiornesounltysaonbdtaairedbeblievtehdeto

overwhosemethodswe havenocontrol.It istheuser'sresponsibilityto

determinesuitabilityfortheuser'spurposeofanyproductionmethodsmentioned

hereinandtoadoptsuchprecautionsasmaybeadvisablefortheprotectionof

prodpertyatnhderofopf.erIsnonlishatgaoifnsttanfyohreazoairdgs,thHatnmkaeylbCeirnpvolvetidointsheehcaifnicdlilnlg

Henkel Americas    Henkel Europe    Henkel AsiaPacific+860.571.5100    +49.89.320800.1800    +86.20.3623.0506

    Forthemostdirectaccesstolocalsalesandtechnicalsupportvisit:loctite.net